可應用于碳纖維預浸帶復合材料、高檔不粘鍋涂層、化工醫藥防腐噴涂、3D打印增材制造、環氧樹脂增韌劑和碳纖維上漿劑等加工助劑、鋰電薄膜等領域，適合靜電噴涂、模壓成型、SLS增材制造等工藝。
PEKK powder can be used for carbon fiber prepreg,high-grade non-stick pan coating,chemicaland pharmaceutical corrosion resistence coating,3D printing additive manufacturing,epoxyresin toughening agent,carbon fiber sizing agent and other plastic processing additives,lithiumelectric film coating,etc.It is suitable for electrostatic coating,heat-press molding,SLS additivemanufacturing and other processing methods.
PEKK 粉末產品牌號規格表
PEKK powder product series profile
項 目 | 單位 | 測試方法 | CC 5601-50/20 | CC 5801-50/20 |
一般性能 General performance | ||||
密度 Density | g/cm3 | ASTM D792 | 1.28 | 1.28 |
熔融指數 MFR@380℃,5Kg | g/10min | ISO 1133 | ≥80 | 30-50 |
機械性能 Mechanical properties | ||||
拉伸強度 Tensile strength | MPa | ASTM D638 | 90 | 90 |
拉伸模量 Tensile modulus | GPa | ASTM D638 | 3.1 | 3.1 |
斷裂伸長率 Elongation at break | % | ASTM D638 | ≥100 | ≥200 |
彎曲強度 Flexural strength | MPa | ASTM D790 | 120 | 120 |
彎曲模量 Flexural sodulus | GPa | ASTM D790 | 2.5 | 2.5 |
熱性能 Thermal performance | ||||
玻璃化轉變溫度 | ℃ | DSC | 155 | 155 |
熔融溫度 Meltingtemperature(Tm) | ℃ | DSC | 305 | 305 |
以上規格僅為部分典型規格牌號，KSTONE 有能力提供更多適合市場及客戶需求的等級。具體信息請咨詢產品經理。
suitable for the needs of market and customer.Please consult the product manager for details.
?靜電噴涂工藝指導
Electrostatic coating processing guide
產品編碼 Product Code | 5601-50/20 |
粒徑 Particle size(D50,μm) | 50/20 |
1.清除制件表面的所有銳邊和毛刺，防止涂層產生針孔等缺陷。 | |
2.首先用表面處理劑或者高溫對金屬制件進行脫脂除油，然后用干凈的氧化鋁砂對制件表面進行噴砂處理。 | |
3.清潔處理過的基材必須加熱至320~350℃并保持約1小時，然后進行粉末噴涂，將粉末均勻涂覆在制件表面，并在320~350℃溫度下烘烤成膜。每層涂層的噴涂時間應控制在10分鐘內，如果表面沉積白色未熔粉末，則須停止該區域的粉末噴涂操作，工件溫度不得低于320℃。 | |
4.重復上述步驟3,直到達到目標厚度，最后冷卻成膜。 | |
5.進行質量檢測，最后入庫待運。 | |
■以上數據為產品的典型數值，不能作為產品驗收標準。
The above data are typical values of products and cannot be used as product acceptance criteria.
■最終制品會受到工況等各種因素的影響，產品介紹所示的數值不能保證完全適用于客戶的使用條件，應用時請客戶做出最終判斷。
The final product will be affected by various factors such as working conditions.The values shown in the product introduction
可以用于薄膜、型材、纖維、共混改性、增材制造，適合擠出成型、注塑成型、3D打印等工藝。
PEKK pellet can be uesd for film,stockshape,fiber,filament,compounding,additivemanufacturing,and suitable for extrusion molding,injection molding,3D plprinting and otherprocessing methods.
PEKK顆粒產品牌號規格表
PEKK pellet product series profile
項 目 | 單位 | 測試方法 | FP-7802UN00 | FP-7802GL30 | FP-7802CA30 | FP-5801UNO0 |
一般性能General performance | ||||||
密度Density | g/cm | ASTM D792 | 1.29 | 1.52 | 1.42 | 1.28 |
熔融指數MFR@380℃,5Kg | g/10min | ISO 1133 | 35 | 15 | 6 | 30-50 |
機械性能Mechanical properties | ||||||
拉伸強度Tensile strength | MPa | ASTM D638 | 105 | 185 | 245 | 90 |
拉伸模量Tensile modulus | GPa | ASTM D638 | 4.0 | 12.8 | 24.9 | 3.1 |
斷裂伸長率Elongation at break | % | ASTM D638 | 20 | 2.1 | 1.5 | ≥200 |
彎曲強度Flexural strength | MPa | ASTM D790 | 170 | 260 | 353 | 120 |
彎曲模量Flexural modulus | GPa | ASTM D790 | 3.8 | 9.0 | 16.4 | 2.5 |
熱性能Thermal performance | ||||||
玻璃化轉變溫度(Tg | ℃ | DSC | 160 | 160 | 160 | 155 |
熔融溫度Melting temperature(Tm) | ℃ | DSC | 350 | 350 | 350 | 305 |
■以上規格僅為部分典型規格牌號， KSTONE 有能力提供更多適合市場及客戶需求的等級。具體信息請咨詢產品經理
The above specifications are only some typical specifications and brands.KSTONE has the ability to provide more grades
suitable for the needs of market and customer.Please consult the product manager for details
?注塑工藝指導
Injection molding processing guide
成型參數 | 產品編碼 | PEKK FP-7802UN00 |
干燥溫度 | Drying temperature ℃ | 150 |
干燥時間 | Drying time(H) | 4 |
噴嘴溫度 | Nozzle temperature℃ | 390~380 |
四區溫度 | Zone 4 ℃ | 390～380 |
三區溫度 | Zone 3 ℃ | 385～365 |
二區溫度 | Zone 2 ℃ | 370～350 |
一區溫度 | Zone1 ℃ | 355～345 |
模具溫度 | Molding Temp.℃ | 210~190 |
■以上數據為產品的典型數值，不能作為產品驗收標準。
The above data are typical values of products and cannot be used as product acceptance criteria.
■最終制品會受到工況等各種因素的影響，產品介紹所示的數值不能保證完全適用于客戶的使用條件，應用時請客戶做出最終判斷。
The final product will be affected by various factors such as working conditions.The values shown in the product introduction can not be guaranteed to be fully applicable to the customer's conditions.Please make final judgment when applying.
本公司采用國內獨家生產的PEKK樹脂，配合美國杜邦、日本大金、旭硝子等國際大品牌氟樹脂原料，配備先進智能氣流粉碎機組、高速混合機和智能數控研磨機等先進加工設備，質量可靠，并可針對特定工況及應用領域定制工藝配方，可適用于烘焙烤具、塑料模具、汽車配件、醫療手術用具等，廣泛應用于食品加工、工業模具、化工醫藥器械、電子電器、汽車機械、航空航天等耐高溫防腐耐磨不沾應用領域。
■KSTONEWT/ST-530是經過PEKK特別改性的特氟龍液體涂料，特別適合工業用高溫防腐不沾耐磨涂層應用，無需任何底漆粘結，與金屬基材的結合力即可非常強勁，同時表面硬度優于普通特氟龍涂層，表面硬度高，耐磨耐刮擦，且涂層經久耐用，耐高溫，耐真空，適用于溫度不超過180℃的干式真空泵、工業器具不沾涂層等領域。
■SP/WP-5100為ETFE粉末涂料用底漆，作為金屬基體和ETFE涂層的過渡層，可顯著提升ETFE與金屬的粘合性，使ETFE涂層可在其耐受溫度下承受極限真空，適用于溫度不超過150℃的反應釜、換熱器等化工醫藥器械、電子電器、汽車機械、航空航天等高耐溫重防腐領域。
■SP/WP-5600/5601為PFA粉末涂料用底漆，WP-5600、WP5601分別對應PFA薄涂和厚涂型，作為金屬基體和PFA涂層的過渡層，可顯著提升PFA與金屬的粘合性，使PFA涂層可在其耐受溫度下承受極限真空，適用于溫度不超過200℃的反應釜、換熱器等化工醫藥器械、電子電器、汽車機械、航空航天等高耐溫重防腐領域。
> PEKK噴涂系列產品
PEKK coating product series profile
產品系列 | 涂層類型 | 最高適用溫度 | 厚度 | 話用工況及應用領過 |
WT/ST 530 | 單層輕防腐 | 200 | 50~200 | 干式真空泵、鋸片、剪切機、園林剪、汽車緊固件，船用螺旋槳、工業烤盤、輸送機、燃料噴射器、咖啡盤加熱器、食品加工刀具、壓縮機鼓風機等風機葉片和底座。 |
SP/WP_ | 多層重防腐 | 150 | 200~1000 | 反應釜、換熱器、冷凝器、儲罐襯里、離心機、泵機等化工醫藥生產設備，電子行業酸氣管道。 |
SP/WP- | 多層防腐不沾 | 180 | 200~1000 | 攪拌罐、攪拌槳、閥門、泵機等化工醫藥設備，生物醫療設備、鞋模、紡織品干燥機、食品加工設備。 |
SP/WP- | 多層重防腐 | 200 | 200~1000 | 蒸餾塔、蒸發器、換熱器、反應釜、攪拌槳、冷凝器、儲罐，離心機等化工醫藥設備，有機硅晶片生產設備，復印機打印機輥筒、特種燈泡、玻璃，食品加工設備。 |
噴涂工件制作要求
Coating workpiece production requirements
工件加工完進行去翻邊、去毛刺，磨圓所有尖銳邊緣，建議最小半徑6mm,確保工件表面平滑,焊縫需滿焊,焊縫處豐滿圓滑,無氣孔、變形、沙眼、盲孔等缺陷，無尖銳突起、凹坑，所有轉角R≥6
+86-0533-2275333
+86-0533-2275320
網址：http://www.2017jerseys.cn/
郵箱：ksxclbgs@163.com
地址：山東省淄博市淄川區雙楊鎮豐泉路139號
在線客服